This printing ink is two component glass ink, meeting the high requirements of the touch screen industry. The cured film has various advantages, such as good adhesion, water resistance, chemical resistance, printability, surface hardness and abradability.
Scope of applications: common glass, tempered glass.
Operation process: Add 1 portion of the TCBT-100B hardener into 10 portions of this ink and dilute the mixture with moderate thinner, then print with the 350～420-mesh halftone.
First coating: baking at 130℃ for 8 min; Second coating: baking at 130℃ for 8 min;
Third coating: baking at 130℃ for 8 min; Last coating: baking at 130～150℃ for 15～20 min.
Technichal parameters are shown in the following table.
Test Items | Test Methods | Test Results |
Fineness | GB/T1724-79 | ≤8μm |
Surface tension | Application criterion of the dyne pen | ≥32dyn/cm |
Ultrasonic washing | Ordinary detergent, 65℃, 2hr | ①Non-foaming;②non-wrinkling;③non-discoloring;④cross-cut adhesion test, 100% |
Boiling resistance | Soaking in 100℃ deionized water for two hours | ①Non-foaming;②non-wrinkling;③non-discoloring;④cross-cut adhesion test, 100% |
High and low temperature humidity and heat cycle | 80℃, 95% RH (8hr); -40℃(2hr); ten cycles in total
| ①Non-foaming;②non-wrinkling;③non-discoloring;④cross-cut adhesion test, 100% |
Hardness | Mitsubishi Pencil at an angle of 45 degrees, 500-gram force, measuring at different locations for 3 times | ≥2H |
Adhesion | Cutting 100 grids, 3M gummed paper, continuously pulling off for 5 times | cross-cut adhesion test, 100% |
Surface resistance | Testing surface resistance at 5 locations (≤80%RH) | ≥1010Ohm |
Acid resistance | Soaking in 25℃ 5% H2SO4 solution for two hours | ①Non-foaming;②non-wrinkling;③non-discoloring;④cross-cut adhesion test, 100% |
Alkali resistance | Soaking in 25℃ 5% NaOH solution for two hours | ①Non-foaming;②non-wrinkling;③non-discoloring;④cross-cut adhesion test, 100% |
Ethanol tolerance | Tester loaded with 200 grams; using the winsey, dipped with over 99% alcohol, to rub back and forth for 100 times | ①Colorfast; ②not tarnishing |
Solvent (Acetone) resistance | Tester loaded with 200 grams; using the winsey, dipped with chemically pure acetone, to rub back and forth for 50 times | ① Colorfast; ②not tarnishing |
Performance features:
Its obvious predominance lies in environmental compliance, good surface tension, good thixotropic structure, medium drying speed and weak corrosion.
Usage:
① Add 1 portion of the matching TCB-100B hardener into 10 portions of the ink and then fully stir the mixture with moderate thinner before printing.
② The recommended baking temperature is 130℃ and the recommended baking time is 15 min. On other conditions, please confirm the feasibility in advance in order not to affect product quality.
③ During the multilayer overprint, in order to ensure the quality, the first coating solidifies after baking at 130℃ for 8 min; the second coating solidifies after baking at 130℃ for 8 min; the last coating solidifies after baking at 130～150 ℃ for 15～20 min.
④ The selection of the thinner types and the thinner dosage depend entirely on the adjustment of printing mesh number, environmental condition and printing effect.
Storage condition:
Before and after using this series of ink, the ink containers should be kept completely sealed in cool and ventilated places to avoid exposure to open fire and high temperature.
Guarantee period:
The guarantee period is one year since the production date. Beyond the deadline, please reconfirm the usability.
Note ①: All the above tolerance test data, derived from our test results, is for your reference only and not listed as guarantee value.
Note ②: This series of ink meets the standard of RoHS2.0, REACH, Halogen and the total test data concerning eight heavy metals.